Low temperature resistance UHMWPE has excellent low temperature resistance, at liquid helium temperature (-269 ℃) still malleable, so it can be used as low-temperature parts of the nuclear industry. UHMWPE health non-toxic, non-toxic health, can be used in contact with food and drugs. UHMWPE nonstick surface adsorption capacity is very weak, and its anti-adhesive plastic does not break ability behind the best sticky PTFE, thus the product surface and other materials difficult to stick breaks. Water absorption UHMWPE low water absorption; generally less than 0.01%, only 1% of the flame retardant PA66 ultra high molecular weight polyethylene sheet, thereby forming generally do before drying. UHMWPE relatively low density compares with other engineering plastics density. UHMWPE has a tensile strength due to structural features necessary orientation toward the stretch, so there is an unmatched ultra high tensile strength, it can be obtained by gel spinning method ultra high modulus and strength of the fibers, the tensile strength of up to 3 ~ 3.5GPa, the tensile modulus of up to 100 ~ 125GPa; fiber strength is all the fibers have so far been commercialized in the highest antistatic UHMWPE plate, the carbon fiber is larger than 4 times, more than 10 large steel wire times, 50% larger than aramid fiber. Ning County Hongbo Machinery Manufacturing Co., Ltd. mainly produces ultra-high molecular weight polyethylene sheet rods, nylon sheet bar, PP sheet bar, PVC sheet chemical products. Advanced design, long life, high load capacity, high productivity, missed, quick to buy! UHMWPE product use temperature 100 ~ 110 ℃. Cold, and can be used at -269 ℃. Density 0.985g / cm3, molecular weight 2,000,000 product, its tensile strength 40MPa, elongation at break of 350%, flexural modulus of 600MPa, Izod notched impact red constantly. The amount of wear (MPC method) 20mm. 1, to improve the wear resistance. UHMWPE sheet of the most striking one is that it has a very high performance ultra high molecular weight polyethylene wear plates, this performance has many engineering applications are very valuable. In the present, all plastic, its wear resistance is the best, even many metal materials (such as carbon steel, stainless steel, bronze, etc.) are not as regular grind it. As the molecular weight of the polyethylene increases, the more such materials wear. 2, a very high impact resistance. When the impact strength UHMWPE sheet and its molecular weight about, a molecular weight of less than 2,000,000, with the molecular weight increase, increased impact strength. 3, ultra-high molecular weight polyethylene sheet is very resistant, and low coefficient of friction, good self-lubricating, is an ideal bearing bushings, slider, lining materials. 4, good chemical resistance. Chemical resistant properties of UHMWPE sheet has a good, in addition to concentrated nitric acid, concentrated sulfuric acid, 5, low water absorption. UHMWPE sheet of water absorption is very low, it is almost non-absorbent, does not swell in water, much less absorbent than nylon. 6, thermal properties. Determined by ASTM (load 4.6kg / cm2) method, heat distortion temperature of 85oC, at a smaller load, temperature up to 90oC, flame retardant ultra high molecular weight polyethylene plate, Yangling UHMWPE plate, macro Bo machinery provided by 宁津宏 Bo Machinery Manufacturing Company Limited.宁津宏 Bo Machinery Manufacturing Co., Ltd. (www.myxcl.net) strong, credible, in Dezhou plastic plate (sheet, section), rods and other industries has accumulated a large number of loyal customers. The company better work attitude and constantly improving innovative ideas will lead Hongbo machinery and you hand into the brilliant, for a better future!